Property		Test Condition	Unit	Standard	Value
Rheological properties
	Mold shrinkage, flow/cross to flow	Value range based on general practical experience	in/in	ASTM D955	0.008
Mechanical properties (23 °C/50 % r. h.)
	Flexural modulus	73 °F	lb/in²	ASTM D790	15000
	Flexural modulus	158 °F	lb/in²	ASTM D790	5000
	Tensile strength		lb/in²	ASTM D412	6000
	Ultimate elongation		%	ASTM D412	400
	Tensile stress at 50 % elongation		lb/in²	ASTM D412	1400
	Tensile stress at 100 % elongation		lb/in²	ASTM D412	1600
	Tensile stress at 300 % elongation		lb/in²	ASTM D412	3500
	Compression set, as molded	22 h at 73 °F	%	ASTM D395-B	22
	Compression set, as molded	22 h at 158 °F	%	ASTM D395-B	75
	Compression set, post-cured	22 h at 73 °F; post-cured 16 h at 230 °F	%	ASTM D395-B	20
	Compression set, post-cured	22 h at 158 °F; post-cured 16 h at 230 °F	%	ASTM D395-B	40
	Compressive load	2% deflection	lb/in²	ASTM D575	130
	Compressive load	5% deflection	lb/in²	ASTM D575	305
	Compressive load	10% deflection	lb/in²	ASTM D575	550
	Compressive load	15% deflection	lb/in²	ASTM D575	775
	Compressive load	20% deflection	lb/in²	ASTM D575	1000
	Compressive load	25% deflection	lb/in²	ASTM D575	1215
	Compressive load	50% deflection	lb/in²	ASTM D575	3125
	Tear strength, Die C		lbf/in	ASTM D624	725
Thermal properties
	Glass transition temperature	DMA=Dynamic Mechanical Analysis	°F	DMA	-40
	Low-temperature brittle point		°F	ASTM D746	< -90
	Vicat softening temperature		°F	ASTM D1525	240
Other properties (23 °C)
	Specific gravity		-	ASTM D792	1.14
	Shore hardness		D Scale	ASTM D2240	50
	Taber abrasion	H-18 wheel; 1,000-g; 1,000 cycles	mg Loss	ASTM D3489	60
	Bayshore resilience		%	ASTM D2632	35

Disclaimer

Aromatic polyether-based grade thermoplastic polyurethane with approximate Shore D hardness of 45 for injection molding, extrusion, and blow molding., Typical applications include boots, non-regulated animal identification tags, seals, pads, tubing, cable jacketing, sheet, and profiles.